產(chǎn)品參數(shù)

　　性能項(xiàng)目試驗(yàn)條件[狀態(tài)]測(cè)試方法測(cè)試數(shù)據(jù)數(shù)據(jù)單位

　　基本性能吸水量浸泡均衡點(diǎn)+73℉(+23℃)ASTM D5700.90%

　　吸水量Equil.50%R.h.+73℉(+23℃)ASTM D5700.22%

　　密度ASTM D7921.42

　　吸水量24hrs浸泡+73℉(+23℃)ASTM D5700.25%

　　物理性能絕緣強(qiáng)度Short Time,90 milsASTM D149500V/mil

　　絕緣系數(shù)系數(shù) +73℉(+23℃)102to106HzASTM D1503.7

　　絕緣強(qiáng)度Short Time,2.3mmASTM D14919.7MV/m

　　擴(kuò)散因數(shù)+73℉(+23℃)106HzASTM D1500.005

　　摩擦系數(shù)+73℉(+23℃)靜態(tài)0.20ThrustWasherTest3

　　摩擦系數(shù)+73℉(+23℃)動(dòng)態(tài)ThrustWasherTest30.35

　　電阻系數(shù)+73°F(+23℃)0.2%H2OASTM D2571015ohm-cm

　　機(jī)械性能伸張強(qiáng)度+122℃ASTM D63826.2MPa

　　撓曲系數(shù)+212℉在25℃下130MPsi

　　彎曲降服強(qiáng)+23℃ASTM D79098.6MPa

　　撓曲系數(shù)+122℃在25℃下620MPa

　　伸張強(qiáng)度+212℉ASTM D6385.2Mpsi

　　lzod沖擊強(qiáng)度+23℃ASTM D256123j/m

　　洛氏硬度ASTM D785M94,R120

　　斷裂時(shí)之拉力伸張度+158℉(+70℃)ASTM D638230%

　　伸張強(qiáng)度-55℃ASTM D638101MPa

　　撓曲系數(shù)-68℉在25℃下530MPsi

　　撓曲系數(shù)-55℃在25℃下3650MPa

　　無(wú)切口沖擊程度+23℃D256>5300(no break)j/m

　　撓曲系數(shù)+70℃在25℃下1550MPa

　　撓曲系數(shù)+250℉在25℃下90MPsi

　　壓縮應(yīng)力縮應(yīng)力 +73°F@1%Def.ASTM D6955.2MPsi

　　彈性系數(shù)+23℃ASTM D6383100MPa

　　彎曲降服強(qiáng)+73℉ASTM D79014.3MPsi

　　lzod沖擊強(qiáng)度40℃ASTM D25696.1j/m

　　撓曲系數(shù)+73℉在25℃下380MPsi

　　伸張強(qiáng)度+100℃ASTM D63835.9MPa

　　壓縮應(yīng)力+23℃@10%Def.ASTM D695124MPa

　　彈性系數(shù)+73℉ASTM D638450MPsi

　　斷裂時(shí)之拉力伸張度-68℉(-55℃)ASTM D63838%

　　無(wú)切口沖擊程度+73℉ASTM D256>100(no break)ft.lb/in

　　壓縮應(yīng)力+23℃@1%Def.ASTM D69535.9MPa

　　斷裂時(shí)之拉力伸張度+212℉(+100℃)ASTM D638>260%

　　lzod沖擊強(qiáng)度-40℉ASTM D2561.8ft.lb/in

　　伸張強(qiáng)度+23℃ASTM D-63868.9MPa

　　負(fù)載下之變形2000psi@+122℉(14Mpa@50℃ASTM D6210.5%

　　伸張強(qiáng)度-68℉ASTM D63814.7MPsi

　　撓曲系數(shù)+23℃在25℃下2620MPa

　　伸張強(qiáng)度+158℉(+70℃)ASTM D6386.9MPsi

　　伸張強(qiáng)度+70℃ASTM D63847.5MPa

　　彎曲疲勞忍耐限度+73℉ASTM D6714.7MPsi

　　伸張強(qiáng)度+73℉ASTM D63810.0MPsi

　　壓縮應(yīng)力+73°F@10%Def.ASTM D69518.0MPsi

　　剪力+73℉ASTM D7329.5MPsi

　　撓曲系數(shù)+100℃在25℃下895MPa

　　剪力+23℃ASTM D73265.5MPa

　　拉力沖擊抵抗力+73℉D1822Long170ft.lb/in2;

　　斷裂時(shí)之拉力伸張度+73℉(+23℃)ASTM D63875%

　　伸張強(qiáng)度+250℉ASTM D6383.8MPsi

　　lzod沖擊強(qiáng)度+73℉ASTM D2562.3ft.lb/in

　　拉力沖擊抵抗+23℃D1822Long350KJ/m2

　　彎曲疲勞忍耐限度+23℃ASTM D67132.4MPa

　　撓曲系數(shù)+158℉在25℃下225MPsi

　　斷裂時(shí)之拉力伸張度+250℉(+122℃ASTM D638>260%

　　電氣性能電弧抵抗力120mil(3.1mm)ASTM D495220no trackingSec.

　　熱性能熔點(diǎn)ASTM D2133347°F

　　熱變形溫度1.8MPaASTM D648136℃

　　線性熱膨脹系數(shù)+85 to +140℉ASTM D6966.810-5in/in.℉

　　線性熱膨脹系數(shù)+140 to +220℉ASTM D6967.610-5in/in.℉

　　線性熱膨脹系數(shù)-40 to +85℉ASTM D6965.810-5in/in.℉

　　線性熱膨脹系數(shù)-40 to +29℃ASTM D69610.410-5m/m.℃

　　熱變形溫度264psiASTM D648277℉

　　線性熱膨脹系數(shù)+60 to +104℃ASTM D69613.710-5m/m.℃

　　熔點(diǎn)ASTM D2133175℃

　　熱傳導(dǎo)系數(shù)0.37W/mk

　　熱變形溫度0.5MpaASTM D648172℃

　　熱傳導(dǎo)系數(shù)2.6BTU-in/hr

　　線性熱膨脹系數(shù)+220 to +300℉ASTM D6968.310-5in/in.℉

　　熱變形溫度66psiASTM D648342℉

　　線性熱膨脹系數(shù)+104 to +150℃ASTM D69614.910-5m/m.℃

　　線性熱膨脹系數(shù)+29 to +60℃ASTM D69612.210-5m/m.℃

　　其它性能可燃燒性UL9494HB