點擊圖片查看大圖
| 吸水率 | --- | ASTM D-570 | 0.15 | % | |||||||||||
| 熔體流動速率 | --- | ASTM D-1238 | 7 | g/10min | |||||||||||
| 物理性能 | 模具收縮率 | 3.2mm | ASTM D-955 | 5-7 | 10-3 | ||||||||||
| 比重 | --- | ASTM D-792 | 1.21 | --- | |||||||||||
| 阻燃性 | --- | UL 94 | V-2 | --- | |||||||||||
| 阻燃性 | --- | UL 94 | 1.6 | mm | |||||||||||
| 阻燃性 | --- | UL 94 | V-0 | --- | |||||||||||
| 阻燃性 | --- | UL 94 | 3.0 | mm | |||||||||||
| 機械性能 | 缺口沖擊強度 | 23℃ | ASTM D-256 | 640 | J/m | ||||||||||
| 洛氏硬度 | --- | ASTM D-785 | 118 | --- | |||||||||||
|
|
|
|
|
|||||||||||
| 斷裂伸長率 | --- | ASTM D-638 | 90 | % | |||||||||||
| 彎曲強度 | --- | ASTM D-790 | 91 | MPa | |||||||||||
| 彎曲模量 | --- | ASTM D-790 | 3250 | MPa | |||||||||||
| 電氣性能 | 損耗因數 | 60Hz | ASTM D-150 | 0.0009 | --- | ||||||||||
| 損耗因數 | 1MHz | ASTM D-150 | 0.01 | --- | |||||||||||
| 介電常數 | 60Hz | ASTM D-150 | 3.01 | --- | |||||||||||
| 介電常數 | 1MHz | ASTM D-150 | 2.96 | --- | |||||||||||
| 體積電阻率 | --- | ASTM D-257 | 1.0×1017 | Ω.cm | |||||||||||
| 熱 性 能 | 熱變形溫度 | 0.45MPa | ASTM D-648 | 137 | ℃ |
分類：防靜電PC，導電PC，加纖防火PC，抗紫外線耐候PC，食品級PC,透明PC,半透明PC,光擴散PC, 吹瓶級PC,耐高溫PC,抗(UV)PC通用級PC,耐候級PC,耐寒級PC,增韌級PC,光學級PC,防火級PC,阻燃級PC。
PC 945R性能以及加工
低溫-45度聚碳酸酯無色透明，耐熱，抗沖擊，阻燃BI級，在普通運用溫度內都有出色的機械功用。
密度:1.20－1.22g/cm^3
線膨脹率：3.8×10 cm/cm°C
熔流率(330°C/2.16 kg)
模具溫度注射壓力：50~80、80~130，工藝預熱溫度110~120參數時間/h料桶
23°C, 24 hr 0.20%
飽和, 23°C 0.40%
飽和0.40%
平衡0.20%
模具溫度注射壓力50~80、80~130工藝預熱溫度110~120參數時間/h料桶
電氣化學性能
表面電阻率
玻璃化溫度為145-150℃
脆化溫度-100℃
高運用溫度為135℃
熱變性溫度為115-127℃
可燃性 UL阻燃等級V0、V1、V2、HB厚度3.0mm、2.0mm、1.5mm、0.8mm