點(diǎn)擊圖片查看大圖|
LCP 7130L 美國(guó)杜邦公司 物性數(shù)據(jù) |
|
①原料描述部分 |
|||||
|
②原料技術(shù)數(shù)據(jù) |
|||||
|
性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測(cè)試方法 |
測(cè)試數(shù)據(jù) |
數(shù)據(jù)單位 |
|
|
物理性能 |
比重 |
黑色 |
ASTM D-792 |
1.62 |
--- |
|
泰伯摩擦 |
--- |
ASTM D-1044 |
63 |
mg |
|
|
模縮率 |
流向1.6mm |
ASTM D-955 |
-0.1 |
% |
|
|
模縮率 |
流向3.2mm |
ASTM D-955 |
0 |
% |
|
|
模縮率 |
橫向1.6mm |
ASTM D-955 |
0.9 |
% |
|
|
機(jī)械性能 |
模縮率 |
橫向3.2mm |
ASTM D-955 |
0.8 |
% |
|
洛氏硬度 |
Scale M |
ASTM D-785 |
63 |
--- |
|
|
沖擊下機(jī)械性能 |
--- |
UL 746B |
210 |
oC |
|
|
拉伸強(qiáng)度 |
23℃,1.6mm |
ASTM D-638 |
173 |
MPa |
|
|
拉伸強(qiáng)度 |
23℃,3.2mm |
ASTM D-638 |
150 |
MPa |
|
|
斷裂伸長(zhǎng)率 |
23℃,1.6mm |
ASTM D-638 |
1.6 |
% |
|
|
斷裂伸長(zhǎng)率 |
23℃,3.2mm |
ASTM D-638 |
1.7 |
% |
|
|
拉伸模量 |
23℃,1.6mm |
ASTM D-638 |
19306 |
MPa |
|
|
拉伸模量 |
23℃,3.2mm |
ASTM D-638 |
18000 |
MPa |
|
|
彎曲模量 |
23℃,0.8mm |
ASTM D-790 |
18000 |
MPa |
|
|
彎曲模量 |
23℃,1.6mm |
ASTM D-790 |
14000 |
MPa |
|
|
彎曲模量 |
23℃,3.2mm |
ASTM D-790 |
13100 |
MPa |
|
|
無(wú)缺口沖擊強(qiáng)度 |
23℃,1.6mm |
ASTM D-4812 |
840 |
j/m |
|
|
無(wú)缺口沖擊強(qiáng)度 |
23℃,3.2mm |
ASTM D-4812 |
555,20%NB |
j/m |
|
|
彎曲強(qiáng)度 |
23℃,0.8mm |
ASTM D-790 |
215 |
MPa |
|
|
彎曲強(qiáng)度 |
23℃,1.6mm |
ASTM D-790 |
192 |
MPa |
|
|
彎曲強(qiáng)度 |
23℃,3.2mm |
ASTM D-790 |
183 |
MPa |
|
|
壓縮強(qiáng)度 |
3.2mm |
ASTM D-695 |
89 |
MPa |
|
|
彎曲疲勞 |
3.2mm，69MPa |
ASTM D-671 |
2667 |
cycle |
|
|
IZOD沖擊強(qiáng)度 |
23℃,0.8mm |
ASTM D-256 |
400,40%NB |
j/m |
|
|
IZOD沖擊強(qiáng)度 |
23℃,1.6mm |
ASTM D-256 |
170 |
j/m |
|
|
IZOD沖擊強(qiáng)度 |
23℃,3.2mm |
ASTM D-256 |
225 |
j/m |
|
|
電氣性能 |
介電強(qiáng)度 |
1.6mm逐步 |
ASTM D-149 |
31 |
KV/mm |
|
介電強(qiáng)度 |
23℃,1.6mm短時(shí)間 |
ASTM D-149 |
35 |
KV/mm |
|
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。